sdi gs 80 - capsules
Optimal handling characteristics
GS-80’s consistent mix, ease of loading, placement in preparations, condensability, burnishability, quality of interproximal contact, carvability, and setting characteristics ensure the fi nal restorations meet the needs of the operator.
High compressive strength
GS-80’s high compressive strength minimizes the risk of fracturing the restoration.(1) High compressive strength ensures a tough and durable long lasting restoration.
Positive dimensional change
GS-80’s positive dimensional change ensures excellent sealing qualities at the margins.(1) Negative values can contribute to post operative sensitivity
Capsule system
The SDI capsule system is designed to give consistent and accurate mixes every mix.
Greater choice of setting times and larger choice of capsule sizes
The working and setting times allow large restorations to be condensed and carved without diffi
The technically advanced, non-gamma 2 admix amalgam at an affordable price. GS-80’s high strength ensures longevity and patient satisfaction. The alloy to mercury ratio varies between 1/0.85 and 1/0.94 depending on the size and setting time, i.e. 45.9% to 48.5% by weight mercury. The compressive strength of GS-80 at 24 hours is 510 MPa, and the dimensional change during hardening is +0.02%.
COMPOSITION:
- Alloy Particle: Spherical and Lathe Cut
- Compressive strength -1 hour: 225MPa (32,625psi)
- Compressive strength -24 hours: 510MPa (73,950psi)
- Diametral tensile strength -1 hour: 22MPa (3,190psi)
- Diametral tensile strength -24 hours: 54MPa (7,830psi)
- Static creep -7 days: 0.1%
- Dimensional change -24 hours: +2µm/cm
PACKAGING
Jar of 50 capsules