Prevest Micron Luting Glass ionomer luting cement

FEATURES

  • Translucent shade.
  • Very low film thickness
  • High fluoride release.
  • Low solubility

 

DESCRIPTION

Micron Luting is convenient self curing , fine particle, fluoride releasing, glass ionomer luting cement for crowns , bridges, securing inlays, onlays, post and orthodontic brackets.

Micron Luting is the Ideal radiopaque, self curing translucent, particle glass-ionomer luting material with excellent tooth adhesion high fluoride release and flowability, It is useful for a wide range of clinical applications. Micron luting is available in a universal light yellow shade in Powder and Liquid Kits.


INDICATION:-

  • Cementation of posts and screws
  • Attachment of metals orthodontics bands
  • Cementation of inlays, onlays and crowns

ADVANTAGES:

* High fluoride release.
* Low solubility.
* Translucent shade.
* Very low film thickness

 

KEY SPECIFICATION

Composition:

Powder: Fluoro Alumina Silicate Glass Powder
Liquid: Polyacrylic Acid Liquid (Thin Viscosity)

Powder/Liquid ratio (0.19/0.12),

  • Mixing time (min. sec) : 45-60 seconds,
  • setting time (min. sec) : 2min 30sec, (at 23±1°C from start of mixing)
  • Final finishing commencing time (after seating the restoration) : 5 min.

CONTRAINDICATION:
1)Micron Luting should not be used if the patient is known to be allergic to any of the ingredient used.
2) Do not apply the material directly onto areas near the pulp or onto the exposed pulp as irritation may occur.

Storage Conditions :
  • Store at temperature between 10°C to 24°C. Close the cap carefully after use. Keep away from moisture. Shelf life not affected after opening if stored in a cool dry place.

 

PACKING

Powder- Liquid Kit.,
* 1 X Powder Jar 15g
* 1 X Liquid Bottle 10ml
* 1 X Mixing Pad.
* 1 X Spoon.

Customer Reviews

Be the first to write a review
0%
(0)
0%
(0)
0%
(0)
0%
(0)
0%
(0)
.