Harvard Zinc Phosphate Cement

Harvard Zinc Phosphate Cement

Zinc phosphate cement for permanent luting of crowns and bridges, inlays and onlays on natural core and for luting supraconstructions on implants  

Indications:

• For permanent luting of crowns and bridges, inlays and onlays on natural core and for luting supraconstructions on implants.
• For crowns, bridges, inlays and onlays made of: zirconia aluminium oxide lithiumdisilicate silicate for conventional gold and non-precious metals

 Properties:

1. High compressive strength
2. Low film thickness
3. Good biocompatibility
4. Easy and safe application
5. Unmatched price performance ratio
6. No curing shrinkage 

Features

• High compressive strength and low film thickness
• Good biocompatibility
• Easy and safe application
• Unmatched price / performance ratio for luting and lining materials
• Applicable for: Zirconoxid Ceramic, Silikat Ceramic, Aluminiumoxid Ceramic, Gold and non-metals
• Cement according to DIN EN ISO 9917-1
• Available in two setting times: normal and fast setting

Key Specification

Composition:

• 1 g powder contains: 860 mg zinc oxide, 86 mg magnesium oxide;
• 1 g liquid contains: 560 mg o-phosphoric acid.

Dispensing Instructions:

• Fixation consistency: 1.5 g powder : 1.0 g liquid
• Cavity lining consistency: 2.1 g powder : 1.0 g liquid
• Dispensing and testing climate for testing in accordance with DIN EN ISO 9917:
• Mix quantities indicated at 23 ± 1°C and a relative humidity of 50 ± 10%.
  
  

Mixing Time: 90 seconds

Processing Time: from start of mixing (at 23 °C, 72 °F):

For fixation: 3 minutes

For cavity lining: 2 minutes Setting Time from end of mixing: 5:00 – 8:00 minutes

HARVARD CEMENT normal setting - Do not use after the expiration date. -

Storage temperature: 2–28 °C (36-82 °F).

PACKAGING

Harvard Zinc Phosphate Set Powder 35gm + Liquid 15ml

• 1 x 35gm Powder
• 1 x 15ml Liquid

Harvard Zinc Phosphate Set Powder 100g + Liquid 40ml

• 1 x 100gm Powder
• 1 x 40ml LiquidHarvard Zinc Phosphate Cement